In situ synthesis of polytungstate anion-pillared Ni-Al hydrotalcite

WANG LiQing1,2;LIU HongTao1;LI XiuYan2;FU JiQuan2;XU ChunYan1

Journal of Beijing University of Chemical Technology ›› 2008, Vol. 35 ›› Issue (2) : 24-28.

PDF(922 KB)
Welcome to Journal of Beijing University of Chemical Technology, Today is July 12, 2025
Email Alert  RSS
PDF(922 KB)
Journal of Beijing University of Chemical Technology ›› 2008, Vol. 35 ›› Issue (2) : 24-28.
化学与化学工程

In situ synthesis of polytungstate anion-pillared Ni-Al hydrotalcite

  • WANG LiQing1,2;LIU HongTao1;LI XiuYan2;FU JiQuan2;XU ChunYan1
Author information +
History +

Abstract

A terephthalate anion-pillared Ni-Al hydrotalcite-like layered double hydroxide (LDH) was synthesized on the surface and within the pores of γ-Al2O3 by in situ crystallization and a polytungstate anion-pillared hydrotalcite was subsequently obtained by ion-exchange. The materials were characterized by XRD, BET, FT-IR and TG-DTA. XRD indicated that the replacement of the terephthalate anion by the polytungstate anion had little effect on the structure. FT-IR spectra suggested that a strong interaction was present between γ-Al2O3 and the hydrotalcite. N2 adsorption measurements showed that the surface area of the LDHs/γ-Al2O3 composite was 247m2/g, higher than that of γ-Al2O3 (219m2/g), whilst the pore diameter (3-4nm) was lower than that of γ-Al2O3 (2-11nm). Therefore, it can be concluded that nanosized crystals of LDHs are located on both the surface and within the pores of γ-Al2O3. The properties of the material make it a good candidate for a hydrodesulfurization catalyst. 

Cite this article

Download Citations
WANG LiQing1,2;LIU HongTao1;LI XiuYan2;FU JiQuan2;XU ChunYan1
.
In situ synthesis of polytungstate anion-pillared Ni-Al hydrotalcite[J]. Journal of Beijing University of Chemical Technology, 2008, 35(2): 24-28

References

[1]Marquevich M, Medina F, Montané D. Hydrogen production via steam reforming of sunflower oil over Ni/Al catalysts from hydrotalcite materials[J]. Catalysis Communications, 2001, 3(2): 119-124.
[2]Lv Liang, He Jing, Wei Min, et al. Factors influencing the removal of flu
oride from aqueous solution by calcined Mg-Al-CO3 layered double hydroxides[J]. Journal of Hazardous Materials, 2006, 133(1-3): 119-128.
[3]Di Cosimo J I, Diez V K, Xu M, et al. Structure and Surface and Catalytic
Properties of Mg-Al Basic Oxides[J]. Journal of Catalysis, 1998, 178(2): 499-510.[4]杜以波, Evans D G, 孙鹏, 等. 阴离子型层柱材料研究进展[J]. 化学通报, 2000, 63(5): 20-23.
[5]刘炳华, 朱海燕, 张惠良,等. 以水滑石及类水滑石为前体制备的Ni、Mg、Al混合氧化物的合成和表征[J]. 无机化学学报, 2005, 21(6): 852-859.
[6]毛纤冰,李殿卿,张法智,等. γ-Al2O3 表面原位合成Ni-Al-CO3LDHs的研究[J]. 无机化学学报, 2004, 20(5):596-601.
[7]杨锡尧, 夏晓球, 吴念祖. 钼酸盐阴离子柱撑镁铝水滑石为前驱物的加氢脱硫催化剂MoO3/Mg(Al)中MoO3的化学状态和分散度[J]. 催化学报, 2001, 22(4):358-360.
[8]Crepaldi E L, Tronto J, Cardoso L P, et al. Sorption of terephthalate anions by calcined and uncalcined hydrotalcite like compounds[J]. Colloids and Surfaces A: Physicochemival Engineering Aspects, 2002, 211: 103-113.
[9]Gardner E, Pinnavaia T J. On the nature of selective olefin oxidation catalysts derived from molybdate and tungstate intercalated layered double hydroxides[J]. Applied Catalysis A: General, 1998, 167: 65-74.
[10]赵芸, 梁吉, 李峰, 等. 层状双金属氢氧化物的热分解及动力学研究[J]. 清华大学学报: 自然科学版, 2004, 44(2): 149-152. 
[11]牟真. 柱撑水滑石及其复合氧化物催化剂的制备与表征[D]. 山东济南: 山东大学, 2005.
PDF(922 KB)

4862

Accesses

0

Citation

Detail

Sections
Recommended

/