熔盐辅助煅烧法制备纳米MgO

  • 施利毅;韩丹丹
作者信息 +

Synthesis of MgO nano-crystallite powders by a molten salt method

  • SHI LiYi;HAN DanDan
Author information +
文章历史 +

摘要

以无水硫酸镁、氨水和月桂酸钠作为原材料,采用醇水体系一步法制备了表面修饰纳米 Mg(OH)2,经熔盐LiNO3辅助煅烧制备纳米MgO。用XRD和FT-IR表征前驱物Mg(OH)2的结构及形貌,通过TG-DTA确定煅烧温度,用XRD和TEM对纳米MgO的结构和形貌进行表征。讨论了氨水浓度、氨水用量、煅烧温度、煅烧时间和熔盐添加量对纳米MgO颗粒尺寸和硬团聚程度的影响。初步认为纳米MgO是通过成核、长大过程形成的。通过调控煅烧时间、煅烧温度、熔盐比例,可以将MgO平均粒径有效控制在20~100nm范围。

Abstract

Surface modified Mg(OH)2 particles have been synthesized by a one-step process using magnesium sulfate, ammonia liquor and sodium laureate as raw materials in alcohol-water systems. MgO nano-crystallite powders were subsequently synthesized by calcination of the Mg(OH)2 precursor using a molten salt method; this process was carried out at different temperatures, for different times, and with different molten salt contents. The structure and morphology of the Mg(OH)2
precursor were characterized by XRD and FT-IR. The effects of varying the calcination temperature and molten salt type were studied by TG-DTA analysis. The structure and appearance of the nanometer-scale MgO were studied by TEM and XRD. The effects of varying ammonia liquor content, ammonia liquor concentration, annealing temperature, annealing time and molten salt content on MgO nano-crystallite powder were investigated. The mechanism of formation of MgO is discussed in terms of nucleation and growth processes. It was found that the average crystallite sizes of the resulting MgO powders could be effectively controlled in the range 20-100nm by changing the calcination temperature, calcination time and molten salt content. 

引用本文

导出引用
施利毅1;韩丹丹2. 熔盐辅助煅烧法制备纳米MgO[J]. 北京化工大学学报(自然科学版), 2008, 35(5): 39-44
SHI LiYi;HAN DanDan. Synthesis of MgO nano-crystallite powders by a molten salt method[J]. Journal of Beijing University of Chemical Technology, 2008, 35(5): 39-44

参考文献

[1]Niu Haixia, Yang Qing, Yu Fei, et al. Simple synthesis of singlecrystalline nanoplates of magnesium oxid[J]. Chinese Journal of Chemical Physics, 2006, 19(5): 438-442. 
[2]Aramendía M A, Borau V, Jiménez C, et al. Influence of the preparation method on the structural and surface properties of various magnesium oxide
and their catalytic activity in the MeerweinPonndorfVerley reaction[J]. Applied Catalysis A: General 2003, 244: 207-215. 
[3]ArendtR H. Molten salt synthesis of single magnetic domain BaFe12O19 and SrFe12O19 crystals[J]. Journal of Solid State Chemistry, 1973, 8(4): 339-347. 
[4]赵鹤云, 杨留方, 朱文杰, 等. SnO2纳米棒的制备及表征[J]. 功能材料, 2005, 36(2): 260-266.

[5]王健, 邓小芝, 邱新平, 等. 熔盐法合成NiO纳米微晶[J]. 无机化学学报, 2006,22(10): 1875-1878. 
[6]蔡宗英, 邢献然, 刘桂荣, 等. 熔盐法合成PbTiO3粉体及其表征[J]. 金属学报, 2006, 42(1): 109-112. 
[7]张冰, 曹传宝, 徐亚杰, 等. 熔盐法合成莫来石晶须[J]. 无机化学学报, 2005,
21(2): 277-280. 
[8]Yan Chenglin, Xue Dongfeng, Zou Longjiang. Fabrication of hexagonal
MgO and its precursors by a homogeneous precipitation method[J]. Materials Research Bulletin, 2006, 41: 2341-2348. 
[9]王相田, 郑乾, 汪瑾, 等. 高纯纳米氢氧化镁制备工艺[J]. 化工学报, 2005, 56(7): 1360-1362.
[10]Li Binjie, Zhang Yudong, Zhao Yanbao, et al. A novel method
for preparing surfacemodified Mg(OH)2 nanocrystallites[J]. Materials Science and Engineering A, 2007, 452-453:302-305.
[11]李强, 高濂, 栾伟玲, 等. 纳米ZnO制备工艺中ξ-电位与分散性的关系[J]. 无机材料学报, 1999, 14(5): 813-817. 
[12]宋锡瑾, 宣锋, 王杰. 纳米氢氧化镁的制备[J]. 应用基础与工程科学学报, 200
6, 14(4): 523-528. 
[13]陈敏涛. 白云石制备纳米氢氧化镁及特殊形貌纳米氧化镁的研究[D]. 长沙: 中
南大学, 1998. 
[14]徐宝强. 阻燃级超微氢氧化镁的制备研究[D]. 昆明: 昆明理工大学,2005. 
[15]Khairallah F, Glisenti A. Synthesis, characterization and reactivity study of nanoscale magnesium oxide[J]. Journal of Molecular Catalysis A:Chem
ical, 2007, 274(1-2):137-147.

PDF(1946 KB)

4649

Accesses

0

Citation

Detail

段落导航
相关文章

/