弹性聚四氟乙烯/聚氨酯共混薄膜的制备与性能研究

  • 刘纵曙;张丽叶*
作者信息 +

Preparation of PTFE/TPU membranes with rebound elasticity

  • LIU Zong-shu;ZHANG Li-ye*
Author information +
文章历史 +

摘要

在分散型聚四氟乙烯树脂(PTFE)中混入热塑性弹性体聚氨酯(TPU),采用二次双向拉伸制备了具有良好弹性的多微孔薄膜,并对薄膜进行弹性性能测试及透射电镜(TEM)和 表面扫描电镜(SEM)观察。结果表明:TPU在PTFE中能够均匀掺混,经二次双向拉伸后PTFE 形成了网状结构,TPU依附在PTFE纤维上也被拉伸成细小纤维,二者共同形成了多微孔薄膜,而且TPU的加入有效地改善了PTFE薄膜的弹性性能。

Abstract

The blend membranes were prepared by introduction of TPU into a dispersive resin PTFE. The morphology and thermal properties of the blends, and the rebound elasticity of the membranes were studied. The transmission electron microscopy(TEM) shows that the TPU is fine dispersed in the blends. The scanning electron microscopy (SEM) micrographs exhibit multi-microporous structures of biaxial stretching P TFE/TPU membranes. The PTFE and the TPU of the membranes were stretched into small fibers. The rebound elasticity of biaxial stretching PTFE/TPU membranes was st udied. The results show that the rebound elasticity and tensile elongation of PT F E membranes are both improved with the increasing of TPU.

引用本文

导出引用
刘纵曙;张丽叶*. 弹性聚四氟乙烯/聚氨酯共混薄膜的制备与性能研究[J]. 北京化工大学学报(自然科学版), 2005, 32(6): 48-51
LIU Zong-shu;ZHANG Li-ye*. Preparation of PTFE/TPU membranes with rebound elasticity[J]. Journal of Beijing University of Chemical Technology, 2005, 32(6): 48-51

参考文献

[1 ]  顾钰良,顾珂里. 层压纺织复合材料的生产应用[J ] .产业用纺织品,2000 ,18 (8) :37 - 39
[2 ]  郭玉海,张建春,张旭东. 聚四氟乙烯薄膜防水透湿层压织物的研究[J ] . 北京纺织,1998 (4) :12 - 14
[3 ]  Li S T ,Arenholz E ,Heitz J ,et al . Pulsed-laser deposition of crystalline teflon ( PTFE) films [ J ] . Applied Surface Science ,1998 ,125(1) :17 - 22
[4 ]  彭少贤,余若冰,陆昶,等. 聚四氟乙烯的表面处理与粘接[J ] . 塑料科技,2000 (5) :5 - 8
[5 ]  黄震,张晓丽. 一种适于提高氟塑料粘接性能的表面改性剂[J ] . 化学与粘合,1999 (2) :66 - 68
[6 ]  徐保国,王建伟,王文浩. 氟塑料表面粘接与应用[J ] .工程塑料应用,1998 (3) :9 - 11
PDF(119 KB)

4175

Accesses

0

Citation

Detail

段落导航
相关文章

/