以丙烯酸为原料,N,N'-亚甲基双丙烯酰胺为交联剂,采用光聚合的方法合成了聚丙烯酸-丙烯酸钠高吸水性树脂,并对光引发剂用量、曝光时间、丙烯酸中和度以及交联剂用量等对光聚合反应的影响和对产物吸水性能的影响进行了研究。所制得的吸水性树脂吸水率达1550mL/g,对0.9%NaCl溶液的吸液率为160mL/g。
Abstract
Photopolymerization provides a simple , fast and easy method in the synthesis of super absorbent resin.In this paper , super absorbent resin composed of poly (acrylic acid-sodium acrylate) was synthesized by exposing NaOH neutralized acrylic acid aqueous solution to UV light in the presence of crosslinking agents N ,N'-methylene bisacrylamide and photoinitiators. The effects of different kinds of photoinitiators and crosslinking agents, polymerization time , concentration of photoinitiators and the degree of neutralization on the properties of the resins were studied. The water absorption rates of the resin for deionized water and 019 % NaCl solution are 1 550 mL/ g and 160 mL/ g , respectively.
{{custom_sec.title}}
{{custom_sec.title}}
{{custom_sec.content}}
参考文献
[1 ] 钱 欣,濮阳楠,叶智林. 高吸水性树脂聚丙烯酸钠盐制备工艺研究. 功能高分子学报, 1997 ,10 (2) :184～188
[2 ] 罗 勇. 水溶液聚合法制备聚丙烯酸盐型高吸水聚合物. 合成橡胶工业,1998 , 21(3) :146～149
[3 ] 王晓东,王仁远,时 钧. 丙烯酸与2-丙烯酰胺-2-甲基丙烯酸共聚合成高吸水性树脂的研究. 石油炼制与化工,1998 ,29 (12) :13～16
[4 ] Mikita M , Tanioku S , Takayasu T. Process for preparing dry solid water absorbing polyacrylate resin. USP4703067. 1987210227
[5 ] Aoki S , Yamasaki H. Process for preparation of spontaneously-crosslinked alkali metal acrylate polymers. USP4093776. 1998206206
[6 ] 田大听,过俊石,谢淋泉. 反相悬浮聚合法合成超强吸水剂. 应用化学,1997 ,14 (5) :15～18
[7 ] 林润雄,黄毓礼,牛爱杰. 丙烯酸-丙烯酸钠共聚合成高吸水性树脂的研究. 北京化工大学学报,1998 ,25(1) :35～38
[8 ] 路建美,朱秀林,纪顺俊,等. 二元共聚高吸水性树脂的合成及性能. 石油化工,1998 ,27 (5) :332～335
[9 ] 徐相凌,张志成,费 宾,等. 丙烯酸钠反相乳液聚合.高分子学报,1998 (2) :134～38
[10 ] 邹新禧. 超强吸水剂. 北京:化学工业出版社,1991.203～206
{{custom_fnGroup.title_cn}}
脚注
{{custom_fn.content}}
PDF(100 KB)